Investigation of Mechanical Properties of TiN/TiCN/TiC Multilayer Thin Films Coated on Ti6Al4V Substrate

Authors

  • Abbas Razmi University of Atatuk- Facultu of Engineering- Mechanical Engineering Department
  • Ruhi Yeşildal University of Atatuk- Facultu of Engineering- Mechanical Engineering Department

Keywords:

Magnetron sputtering, TiN/TiCN/TiC film, Ti6Al4V, Scratch, Nanoindentation

Abstract

This study addresses the improvement of hardness and scratch resistance provided by TiN/TiCN/TiC multilayer thin films on Ti6Al4V and Silicon (Si) substrates using magnetron sputtering. X-ray diffraction (XRD), scanning electron microscopy (SEM), and nanoindentation and scratch tests have been carried out in order to characterize the film layer in terms of structural, chemical, and mechanical properties. The cubic and polycrystalline structure of TiN/TiCN/TiC films were confirmed by the XRD analysis. SEM cross-sectional images revealed that the coating has dense and columnar structure with a thickness of 3.065 μm and had formed a good adhesion to the substrate. Hardness and critical load values of the coated Ti6Al4V substrate, as obtained from the scratch and nanoindentation test, were 19.96 GPa and 26 N, respectively.

Downloads

Published

2021-07-15

Issue

Vol. 5 No. 1 (2021): The Marie Curie Issue

Section

Articles

License

The authors keep the copyrights of the published materials with them, but the authors are aggee to give an exclusive license to the publisher that transfers all publishing and commercial exploitation rights to the publisher. The puslisher then shares the content published in this journal under CC BY-NC-ND license.

How to Cite

Investigation of Mechanical Properties of TiN/TiCN/TiC Multilayer Thin Films Coated on Ti6Al4V Substrate. (2021). International Journal of Innovative Research and Reviews, 5(1), 21-25. http://www.injirr.com/index.php/injirr/article/view/68